Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150–550 °C

Baoquan Xue; Jibo Tan; Ziyu Zhang; Xiang Wang; Xinqiang Wu; En-Hou Han; Wei KE

doi:10.1016/j.ijfatigue.2022.107344

journal article Feb 01, 2023

Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150–550 °C

Baoquan Xue Jibo Tan Ziyu Zhang

Xiang Wang

Xinqiang Wu En-Hou Han Wei KE

International Journal of Fatigue Vol. 167 pp. 107344 · Elsevier BV

View at Publisher Save 10.1016/j.ijfatigue.2022.107344

Topics

No keywords indexed for this article. Browse by subject →

References

48

[1]

Old "Liquid metal embrittlement of nuclear materials" J Nucl Mater (1980) 10.1016/0022-3115(80)90136-1

[2]

Martinelli "Corrosion issues in lead-cooled fast reactor (LFR) and accelerator driven systems (ADS)" Nucl Corrosion Sci Eng (2012)

[3]

Bassini "Material Performance in Lead and Lead-Bismuth Alloy" In: Comprehensive Nuclear Materials (2020)

[4]

Corrosion behavior of T91 steel in liquid lead-bismuth eutectic at 550 °C: Effects of exposure time and dissolved oxygen concentration

Zhaoguang Zhu, Qiang Zhang, Jibo Tan et al.

Corrosion Science 2022 10.1016/j.corsci.2022.110405

[5]

Environmental degradation of structural materials in liquid lead- and lead-bismuth eutectic-cooled reactors

Xing Gong, Michael P. Short, Thierry Auger et al.

Progress in Materials Science 2022 10.1016/j.pmatsci.2022.100920

[6]

Fernandes "Failure by liquid metal induced embrittlement" Eng Failure Anal (1994) 10.1016/1350-6307(94)90029-9

[7]

A Review of Recent Advances in the Understanding of Liquid Metal Embrittlement

David G. Kolman

Corrosion 2019 10.5006/2904

[8]

Shchukin "Analysis of liquid metal embrittlement in materials" Mendeleev Commun (2019) 10.1016/j.mencom.2019.11.040

[9]

Nema "Application of Accelerators for Nuclear Systems: Accelerator Driven System (ADS)" Energy Proc (2011) 10.1016/j.egypro.2011.06.080

[10]

Handbook on Lead-bismuth Eutectic Alloy and Lead Properties, Materials Compatibility, Thermalhydraulics and Technologies, 2007 Edition, Nuclear Energy Agency, OECD 2007, NEA No. 6195.

[11]

Gong "The role of oxide films in preventing liquid metal embrittlement of T91 steel exposed to liquid lead-bismuth eutectic" J Nucl Mater (2018) 10.1016/j.jnucmat.2018.07.018

[12]

Gong "Temperature dependence of liquid metal embrittlement susceptibility of a modified 9Cr–1Mo steel under low cycle fatigue in lead–bismuth eutectic at 160–450 °C" J Nucl Mater (2016) 10.1016/j.jnucmat.2015.06.021

[13]

Verma "Low cycle fatigue behavior of modified 9Cr-1Mo steel at 300 °C" Mater Sci Eng A (2018) 10.1016/j.msea.2017.12.105

[14]

Verma "Deformation behavior of modified 9Cr–1Mo steel under low cycle fatigue at 600 °C" Mater Charact (2017) 10.1016/j.matchar.2017.06.024

[15]

Srinivas "Dynamic Strain Ageing Behaviour of Modified 9Cr-1Mo Steel Under Monotonic and Cyclic Loading" Proc Eng (2017) 10.1016/j.proeng.2017.04.155

[16]

Verma "Low cycle fatigue behavior of modified 9Cr–1Mo steel at room temperature" Mater Sci Eng A (2016) 10.1016/j.msea.2015.11.060

[17]

Low-cyclic fatigue behavior of modified 9Cr–1Mo steel at elevated temperature

Krishna Guguloth, S. Sivaprasad, D. Chakrabarti et al.

Materials Science and Engineering: A 2014 10.1016/j.msea.2014.02.076

[18]

Zhou "Influence of dynamic strain aging pre-treatment on the low-cycle fatigue behavior of modified 9Cr–1Mo steel" Int J Fatigue (2013) 10.1016/j.ijfatigue.2012.07.011

[19]

Mariappan "Dynamic strain aging behavior of modified 9Cr–1Mo and reduced activation ferritic martensitic steels under low cycle fatigue" J Nucl Mater (2013) 10.1016/j.jnucmat.2012.12.049

[20]

Nani Babu "Investigation on influence of dynamic strain ageing on fatigue crack growth behaviour of modified 9Cr–1Mo steel" Int J Fatigue (2012) 10.1016/j.ijfatigue.2012.02.022

[21]

Avalos "Dynamic strain aging effects on low-cycle fatigue of AISI 430F" Mater Sci Eng A (2009) 10.1016/j.msea.2009.01.047

[22]

Li "Stress–strain behavior on tensile and low cycle fatigue tests of JLF-1 steel at elevated temperature in vacuum" Fusion Eng Des (2006) 10.1016/j.fusengdes.2006.07.055

[23]

Huang "Dynamic strain aging and grain size reduction effects on the fatigue resistance of SA533B3 steels" J Nucl Mater (2004) 10.1016/j.jnucmat.2003.09.009

[24]

Verma "Dynamic strain ageing, deformation, and fracture behavior of modified 9Cr–1Mo steel" Mater Sci Eng A (2015) 10.1016/j.msea.2014.10.011

[25]

Dmukhovskaya "A phenomenological model of embrittlement of metals under conditions of the adsorption action of liquid metal media" Sov Mater Sci (1982) 10.1007/bf00729424

[26]

Dmukhovskaya "Effect of lead on the fracture of Armco iron" Sov Mater Sci (1979)

[27]

Popovich "Mechanisms of liquid-metal embrittlement" Sov Mater Sci (1979)

[28]

Popovich "Rebinder effect in the fracture of Armco iron in liquid metals" Sov Mater Sci (1978)

[29]

Gong "Effect of liquid metal embrittlement on low cycle fatigue properties and fatigue crack propagation behavior of a modified 9Cr–1Mo ferritic–martensitic steel in an oxygen-controlled lead–bismuth eutectic environment at 350 °C" Mater Sci Eng A (2014) 10.1016/j.msea.2014.09.003

[30]

Chopra OK, Shack WJ. Effect of LWR Coolant Environments on the Fatigue Life of Reactor Materials 2007. p. 7-8.

[31]

Keller "Influence of the temperature on the tensile behaviour of a modified 9Cr–1Mo T91 martensitic steel" Mater Sci Eng A (2010) 10.1016/j.msea.2010.07.021

[32]

Auger "Effect of contact conditions on embrittlement of T91 steel by lead–bismuth" J Nucl Mater (2004) 10.1016/j.jnucmat.2004.07.025

[33]

Tan "Corrosion fatigue behavior of Alloy 690 steam generator tube in borated and lithiated high temperature water" Corros Sci (2014) 10.1016/j.corsci.2014.08.027

[34]

Gong "Low cycle fatigue behavior of a modified 9Cr–1Mo ferritic–martensitic steel in lead–bismuth eutectic at 350 °C – Effects of oxygen concentration in the liquid metal and strain rate" Corros Sci (2015) 10.1016/j.corsci.2015.02.022

[35]

Long "Liquid Pb–Bi embrittlement effects on the T91 steel after different heat treatments" J Nucl Mater (2008) 10.1016/j.jnucmat.2008.02.050

[36]

Sapundjiev "Liquid metal corrosion of T91 and A316L materials in Pb–Bi eutectic at temperatures 400–600 °C" Corros Sci (2006) 10.1016/j.corsci.2005.04.001

[37]

Luo "Honeycomb structure with oxygen-poor pores at the top of magnetite layer on a martensitic steel CLAM exposed to lead-bismuth eutectic at 500 °C" Corros Sci (2022) 10.1016/j.corsci.2022.110410

[38]

Stergar "Influence of LBE long term exposure and simultaneous fast neutron irradiation on the mechanical properties of T91 and 316L" J Nucl Mater (2016) 10.1016/j.jnucmat.2016.02.008

[39]

Long "Investigation of liquid LBE embrittlement effects on irradiated ferritic/martensitic steels by slow-strain-rate tensile tests" J Nucl Mater (2012) 10.1016/j.jnucmat.2011.11.036

[40]

Sapundjiev "A study of the neutron irradiation effects on the susceptibility to embrittlement of A316L and T91 steels in lead–bismuth eutectic" J Nucl Mater (2006) 10.1016/j.jnucmat.2006.05.030

[41]

Van den Bosch "TWIN ASTIR: First tensile results of T91 and 316L steel after neutron irradiation in contact with liquid lead–bismuth eutectic" J Nucl Mater (2010) 10.1016/j.jnucmat.2009.10.012

[42]

Gordon "The Mechanisms of Crack Initiation and Crack Propagation in Metal-Induced Embrittlement of Metals" Metall Trans A (1982) 10.1007/bf02643354

[43]

Hancock "The role of plastic deformation in liquid metal embrittlement" Can Metall Q (2013) 10.1179/cmq.1971.10.3.207

[44]

Robertson "Propagation of a crack filled with liquid metal" Trans Metall Soc AIME (1966)

[45]

J.M.M., Rostoker W, Markus H. Embrittlement by liquid metals. Rheinhold Publishers; 1960.

[46]

Lynch "Progression markings, striations, and crack-arrest markings on fracture surfaces" Mater Sci Eng A (2007) 10.1016/j.msea.2006.09.083

[47]

Lynch "Environmentally assisted cracking: overview of evidence for an adsorption-induced localised-slip process" Acta Mater (1988) 10.1016/0001-6160(88)90113-7

[48]

Westwood "Concerning liquid metal embrittlement, particularly of zinc monocrystals by mercury" Philos Mag (Abingdon) (1963) 10.1080/14786436308213836

Cited By

23

Effect of strain rate on low cycle fatigue behavior of T91 steel hollow specimen filled with liquid lead–bismuth eutectic at 350 °C

Jianhua Ding, Jibo Tan · 2026

Engineering Failure Analysis

Effect of strain rate on low-cycle fatigue behavior of alumina-forming austenitic steel in oxygen-saturated liquid lead-bismuth eutectic at 500°C

Xuanming Shi, Baoquan Xue · 2026

Materials Science and Engineering:...

High-cycle fatigue behavior of T91 steel in air and high oxygen concentration lead-bismuth eutectic at 450 °C

Qiang Lin, Wenlong Zhao · 2026

Journal of Materials Research and T...

Liquid lead-bismuth eutectic enhanced intrusion/extrusion formation and early crack initiation in T91 steel under low-cycle fatigue

Shouwen Shi, Wei Huang · 2025

Corrosion Science

Low-cycle fatigue life prediction of modified 9Cr-1Mo ferritic-martensitic steel in liquid lead–bismuth eutectic environments using a physically-based model

Shouwen Shi, Weibin Li · 2025

Engineering Fracture Mechanics

Insights into the fatigue damage mechanism of T91 steel in liquid lead-bismuth eutectic at 150–550 °C

Baoquan Xue, Wen Wang · 2024

Corrosion Science

Sloshing damping assessment and structural dynamic analysis of perforated structures for heavy liquid metal under seismic excitation

Yalou Chen, Pingjian Ming · 2024

Annals of Nuclear Energy

Metrics

23

Citations

48

References

Details

Published: Feb 01, 2023
Vol/Issue: 167
Pages: 107344
License: View

Authors

Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences , Shenyang 110016 , P.R. China; Southern Marine Science and Engineering Guangdong Laboratory (Zhuhai) , Zhuhai 519000 , P.R. China

W

Wei KE

Cite This Article

Baoquan Xue, Jibo Tan, Ziyu Zhang, et al. (2023). Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150–550 °C. International Journal of Fatigue, 167, 107344. https://doi.org/10.1016/j.ijfatigue.2022.107344

Effect of temperature on low cycle fatigue behavior of T91 steel in liquid lead-bismuth eutectic environment at 150–550 °C

You May Also Like