Analysis of rolling contact fatigue and wear characteristics of aging-treated laminar plasma strip quenching rails

KAI WANG; Taoshuo Bai; Jingmang Xu; Qiantao Ma; Ping Wang; Rong Chen; Yao Qian; Junke Lin; Lu Li

doi:10.1016/j.wear.2024.205245

journal article Mar 01, 2024

Analysis of rolling contact fatigue and wear characteristics of aging-treated laminar plasma strip quenching rails

KAI WANG

Taoshuo Bai Jingmang Xu

Qiantao Ma Ping Wang

Rong Chen

Yao Qian

Junke Lin Lu Li

Wear Vol. 540-541 pp. 205245 · Elsevier BV

View at Publisher Save 10.1016/j.wear.2024.205245

Topics

No keywords indexed for this article. Browse by subject →

References

30

[1]

Zhai "Wear problems of high-speed wheel/rail systems: observations, causes, and countermeasures in China" Appl. Mech. Rev. (2020) 10.1115/1.4048897

[2]

Wang "A feature engineering framework for online fault diagnosis of freight train air brakes" Measurement (2021) 10.1016/j.measurement.2021.109672

[3]

Wang "Severe rail wear detection with rail running band images" Comput. Aided Civ. Infrastruct. Eng. (2023) 10.1111/mice.12948

[4]

Zhu "Study on wear and RCF performance of repaired damage railway wheels: assessing laser cladding to repair local defects on wheels" Wear (2019) 10.1016/j.wear.2019.04.028

[5]

Zeng "Influence of laser dispersed treatment on rolling contact wear and fatigue behavior of railway wheel steel" Mater. Des. (2014) 10.1016/j.matdes.2013.08.041

[6]

Jun "Fracture and fatigue crack growth analyses on a weld-repaired railway rail" Eng. Fail. Anal. (2016) 10.1016/j.engfailanal.2015.11.014

[7]

Shi "Influence of laser strengthening techniques on anti-wear and anti-fatigue properties of rail welding joint" Eng. Fail. Anal. (2019) 10.1016/j.engfailanal.2019.03.012

[8]

Wang "Theoretical study of laminar plasma quenching of rail steel using the fluid-solid-thermal coupling method" Int. J. Therm. Sci. (2022) 10.1016/j.ijthermalsci.2022.107708

[9]

Wang "Study on the mechanism of plasma jet surface hardening of rail steels by using numerical method" Mater. Today Commun. (2022)

[10]

Chang "Wear and chattering characteristics of rail materials by ultrasonic nanocrystal surface modification" Int. J. Precis. Eng. Manuf. (2015) 10.1007/s12541-015-0310-z

[11]

Liu "Effect of surface ultrasonic rolling treatment on rolling contact fatigue life of D2 wheel steel" Materials (2020) 10.3390/ma13235438

[12]

Stump "New functionality of ionic liquids as lubricant additives: mitigating rolling contact fatigue" ACS Appl. Mater. Interfaces (2019) 10.1021/acsami.9b10001

[13]

Li "Ultralow boundary lubrication friction by three-way synergistic interactions among ionic liquid, friction modifier, and dispersant" ACS Appl. Mater. Interfaces (2020) 10.1021/acsami.0c00980

[14]

Xiao "High-temperature tribological properties of coatings repaired by laser additive manufacturing on railway wheel tread damage" Wear (2023)

[15]

Roy "Effect of deposition material and heat treatment on wear and rolling contact fatigue of laser cladded rails" Wear (2018) 10.1016/j.wear.2018.07.001

[16]

Xu "Investigation on wear and damage characteristics of high-speed rail steel with plasma selective quenching" Wear (2021)

[17]

Cao "Investigation on the microstructure and damage characteristics of wheel and rail materials subject to laser dispersed quenching" Appl. Surf. Sci. (2018) 10.1016/j.apsusc.2018.04.210

[18]

An investigation into the microstructure and tribological properties of rail materials with plasma selective quenching

Jingmang Xu, KAI WANG, Ronghe Zhang et al.

Tribology International 2020 10.1016/j.triboint.2019.106032

[19]

Hua "Investigation on WEA fatigue spalling of U71MnG rail material subject to laser quenching surface treatment" Wear (2023)

[20]

Hua "Study on strip WEA wear damage and fatigue spalling of U71MnG rail material by laser quenching treatment" Tribol. Int. (2022) 10.1016/j.triboint.2022.107811

[21]

Ding "Investigation on the rolling wear and damage properties of laser discrete quenched rail material with different quenching shapes and patterns" Surf. Coat. Technol. (2019) 10.1016/j.surfcoat.2019.124991

[22]

Su "Investigation on the rolling wear and damage properties of laser dispersed quenched rail materials treated with different ratios" Tribol. Int. (2019) 10.1016/j.triboint.2019.03.022

[23]

Zhang "The rolling-sliding wear behavior and damage mechanism of the rail steel treated by plasma selective quenching" Surf. Coat. Technol. (2021) 10.1016/j.surfcoat.2021.127908

[24]

Wang "Effect of material non-uniformity and residual stress on wear and transient rolling contact behaviour in laminar plasma quenched (LPQ) rails" Wear (2023) 10.1016/j.wear.2023.204767

[25]

Wang "Surface treatment of rail to enhance rolling contact fatigue and wear resistance: combined spot laminar plasma quenching and tempering method" Construct. Build. Mater. (2023) 10.1016/j.conbuildmat.2023.132832

[26]

Hu "Investigation on wear and rolling contact fatigue of wheel-rail materials under various wheel/rail hardness ratio and creepage conditions" Tribol. Int. (2020) 10.1016/j.triboint.2019.106091

[27]

(1990)

[28]

Xie "Investigation on the rolling contact fatigue behaviors of different laser cladding materials on the damaged rail" J. Tribol. (2021) 10.1115/1.4050690

[29]

Ding "Investigation on the rolling wear and damage properties of laser discrete quenched rail material with different quenching shapes and patterns" Surf. Coat. Technol. (2019) 10.1016/j.surfcoat.2019.124991

[30]

Wang "Effect of material non-uniformity and residual stress on wear and transient rolling contact behaviour in laminar plasma quenched (LPQ) rails" Wear (2023)

Cited By

7

Study on gradient microstructural characteristics and crack propagation mechanisms in plasma-quenched rails and white etching layer containing rails

KAI WANG, Jian Yang · 2025

Tribology International

An investigation into crack initiation and extension mechanism of laminar plasma quenched-tempered rail material with different quenched zones

Hui Zhu, Taoshuo Bai · 2024

Tribology International

Metrics

7

Citations

30

References

Details

Published: Mar 01, 2024
Vol/Issue: 540-541
Pages: 205245
License: View

Authors

K

KAI WANG

Department of Biomedical Informatics, Columbia University, 475 Riverside Dr., Mail Code 7717, New York, NY 10115, USA

Xiangtan University

Kunming University of Science and Technology

Hong Kong Polytechnic University

Cite This Article

KAI WANG, Taoshuo Bai, Jingmang Xu, et al. (2024). Analysis of rolling contact fatigue and wear characteristics of aging-treated laminar plasma strip quenching rails. Wear, 540-541, 205245. https://doi.org/10.1016/j.wear.2024.205245

Analysis of rolling contact fatigue and wear characteristics of aging-treated laminar plasma strip quenching rails

You May Also Like